Double perovskite Cs2AgBiBr6 radiation sensor: synthesis and characterization of single crystals

Single crystals of lead-free halide double perovskite Cs2AgBiBr6 sensor material manifest a remarkable potential for application in radiation detection and imaging. In this study, the purity and crystallinity of solution-grown Cs2AgBiBr6 single crystals with cubic Fm3¯\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$$\overline{3}$$\end{document}m symmetry have been corroborated by powder XRD measurements, while the single crystal XRD patterns reveal the dominant {111} lattice planes parallel to the sample surfaces. A wider range of lower resistivity values (106–109 Ωcm) was obtained from the I-V measurements compared to the 1.55 × 109–6.65 × 1010 Ωcm values from the van der Pauw method, which is typically higher for the Ag than for the carbon paint electrodes. Charge-carrier mobility values estimated from the SCLC method for the carbon paint-Cs2AgBiBr6 (1.90–4.82 cm2V−1 s−1) and the Ag-Cs2AgBiBr6 (0.58–4.54 cm2V−1 s−1) including the density of trap states (109–1010 cm−3) are comparable. Similar values of 1.89 cm2V−1 s−1 and 2.36 cm2V−1 s−1 are derived from the Hall effect measurements for a sample with carbon and Ag electrodes, respectively. The key electrical parameters including the X-ray photoresponse measurements indicate that the Cs2AgBiBr6 samples synthesized in this study satisfy requirements for radiation sensors.