Boron-Modified Anodization of Preferentially Oriented TiO2 Nanotubes for Photoelectrochemical Applications

This study investigates the synthesis and characterization of boron-modified nanotubular titania (NTO) arrays fabricated via a single-step anodizing process with varying concentrations of boric acid (BA). Following anodization, a reductive heat treatment was applied to facilitate the crystallization of the anatase phase in the boron-modified NTO. The effect of the BA concentration on the structural, morphological, and photoelectrochemical (PEC) properties of the NTOs was systematically explored through scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), luminescence, and UV-Vis spectrometry. The introduction of boron during anodization facilitated the formation of sub-bandgap states, thereby enhancing the light absorption and electron mobility. This study revealed the optimal BA concentration that yielded a 3.3-fold enhancement of the PEC performance, attributed to a reduction in the bandgap energy. Notably, the highest incident photon-to-current conversion efficiency (IPCE) was observed for NTO samples anodized at a 0.10 M BA concentration. These findings underscore the promise of boron-modified NTOs for advanced photocatalytic applications, particularly in solar-driven water-splitting processes.